PARADIENE 20 TG <br /> Physical and Mechanical Properties <br /> UNITED STATES TEST STANDARDS CANADA TEST STANDARDS <br /> Property Test Property Test Method <br /> (as Manufactured) Values/Units Method (as manufactured) CSA A123.23-15 <br /> I <br /> Thickness(minimum) 110 mils (2.8 mm) ASTM D5147 Thickness(minimum) 2Values/Units.8mm(IlOmils) <br /> section 6 <br /> Thickness(average) 114 mils (2.9 mm) ASTM D5147 Thickness(average) 2.9 mm(114 mils) <br /> section 6 <br /> 'Peak Load @ 73.40F 30 lbf/inch ASTM D5147 'Peak Load 230C 5.3 kN1m <br /> (230C)(avera9e) (5.3 kN1m) section 7- (73.4*9(average) (30 lbffinch) <br /> 'Peak Load @ 0°F 75 lbf/inch ASTM D5147 'Peak Load @-1 110C 75 Itiffinch <br /> (-180C)(average) (13.2 kN/m) section 7 (OOF)(average) (13.2 kN/m) <br /> 'Elongation @ ASTM D5147 'Elongation @ <br /> Peak Load,73.40F 3% section 7 Peak Load,230C 3% <br /> (230C)(average) (73.40F)(average) <br /> 'Elongation @ ASTM D5147 'Elongation @ <br /> Peak Load,OOF(-180C) 3% section 7 Peak Load,-180C 3% <br /> (average) (OOF)(average) <br /> 'Ultimate Elongation ASTM D5147 'Ultimate Elongation <br /> @ 73,40F(230C) 80% section 7 @ 230C(73.40F) 80% <br /> (average) (average) <br /> 'Tear Strength 40 Itif ASTM D5147 N/A N/A <br /> (average) (0.18 kN) section 8 <br /> Water Absorption ASTM D5147 N/A NIA <br /> (maximum) 1% section 10 <br /> Dimensional Stability ASTM D 5147 Dimensional Stability <br /> (maximum) 0.1% section 11 (maximum) 0.1% <br /> Low Temperature ASTM D5147 Low Temperature <br /> Flexibility(maximum) -1 5OF (-2WC) section 12 Flexibility(maximum) -260C(-15°F) <br /> Compound Stability ASTM D5147 Compound Stability <br /> (minimum) 250°F (121°C) section 16 (minimum) 1210C(250°F) <br /> Coating Thickness- 40 mils(1 mm) ASTM D5147 Coating Thickness- 1 mm(�40 mils) <br /> Back Surface section 17 Back Surface <br /> Cyclic Fatigue Paradiene 20 bonded to Paradiene 30 FIR <br /> with an approved method of attachment <br /> passes ASTM D5849 both as-manufactured <br /> and after heat conditioning according to <br /> ASTM D5147. I <br /> 1. The value reported is the lower of either MD or XD. <br /> The above properties have been validated by PRI and are under continuous follow-up to ensure <br /> compliance. The product has been validated to meet ASTM D6163-08,TYPE 1,GRADE S. <br /> Rev 6/2019 <br />